Technical specifications
Liqcreate Flame Retardant HDT is a rigid off-white photopolymer 3D-printing resin and can be processed on most open resin based 3D-printers. 3D-printed parts from this material can withstand high temperatures (HDT-B upto 257°C / 495°F) without posing a fire hazard due to its self-extinguishing capabilities. The material is perfect for creating parts that need comply with UL94 V0 test standards, such as parts for car interior, railway, airplane and electronics. In addition, it can be excellent for tooling manufacturing aids, connector housings and covers.
| Mechanical Properties | |||
|---|---|---|---|
| Description | Method | UV curing 60 minutes at 60°C[1] | UV curing 120 minutes at 60°C[1] |
| Tensile strength | D638 | 41 MPa | 43 MPa |
| Tensile modulus | D638 | 4.2 GPa | 4.2 GPA |
| Elongation at break | D638 | 1 – 3% | 1 – 3% |
| Flexural strength | D790 | 73 MPa | 67 MPa |
| Flexural modulus | D790 | 4.3 GPa | 4.4 GPa |
| IZOD Impact (notched) | D256A | 13 J/m | 13 J/m |
| IZOD Impact (notched) | ISO 180 | 1,74 kJ/m2 | 1,85 kJ/m2 |
| Water sorption | D570-98 | 0.41% | Â 0.41% |
| Shore D Hardness | D2240 | 88 | 89 |
| HDT-B 0.45 MPa | ISO75 | 237°C / 459°F | 257°C / 495°F |
| HDT-A 1.8 MPa | ISO75 | 137°C / 279°F | 145°C / 293°F |
| Degradation temperature | Internal method | > 250°C2/482°F[2] | > 250°C2/482°F[2] |
[1]Post-cured 60 minutes and 120 minutes with high power LED curing at 60°C in the Wicked Engineering curebox. Values and material properties may vary and depend on individual machine processing, part geometry, print orientation, print settings and post-curing settings. [2] Discoloration Above 200°C.
| Description | Method | UV curing 60 minutes at 60°C[1] |
|---|---|---|
| UL94 Flamability Vertical | Â UL94 V0 | pass at 3,0 mm |
| 12 seconds Vertical Flamability – Appendix F, Part I(a)(1)(ii) | Â FAR 25.853(a) | pass at 1,0 mm |
| 60 seconds Vertical Flamability – Appendix F, Part I(a)(1)(i) | Â FAR 25.853(a) | pass at 5,0 mm |
| Horizontal Flamability – Appendix F, Part I(a)(1)(iv) & (v) | Â FAR 25.853(a) | pass at 1,0 mm |
[2]Flamability tests have been executed by the UL laboratories for the UL94 test and by Aeroblaze Laboratory Inc. for the FAR 25.853(a) flamability for aviation tests.
Tilt screen to see the complete technical specifications table
Excellent HDT and Flame Retardant UL94 V0 properties
Liqcreate Flame Retardant HDT has a high heat deflection temperature (HDT) while maintining its excellent UL94 V0 self extinguishing flame retardant properties.
| Description | Value |
|---|---|
| Appearance | White liquid |
| Viscosity | 2800 mPa.s at 25°C |
| Density | 1.12 g/cm3 |
| Ec (405nm) | 6.25 mJ/cm2 |
| Dp (405nm) | 0.234 mm |
| Ec (385nm) | 3.11 mJ/cm2 |
| Dp (385nm) | 0.095 mm |
More information
Values of Liqcreate Flame Retardant HDT resin may vary and depend on individual machine processing and post-curing. For extra details, download the technical data sheet or user guide.
⤓ Technical Data Sheet  ⤓ Processing instructions  ⤓ User Guide
Processing instructions
New to resin 3D-printing, or a seasoned professional, it is advised to scroll through the Liqcreate Flame Retardant HDT (UL94 V0) resin processing instructions. Detailed information on printing parameters, support settings, cleaning, washing, post-curing, part orientation, shrinkage compensation, minimum wall thickness and other resin behaviour can be found in the link.
| H315: Causes skin irritation. |
| H317: May cause an allergic skin reaction. |
| H318: Causes serious eye damage |
| H410: Very toxic to aquatic life with long lasting effects. |
3D Printer compatibility
Do you want to use Flame Retardant HDT resin? Check if settings for this UL94 V0 resin are available on our website for your printer!
| Printer name | Compatible? |
| Nexa3D XiP | Yes (open license) |
| W2P SolFlex 150 | Yes |
| W2P SolFlex 163FHD | Yes |
| W2P SolFlex 170 | Yes |
| W2P SolFlex 250UHD | Yes |
| W2P SolFlex 350 | Yes |
| W2P SolFlex 363 | Yes |
| W2P SolFlex 650 | Yes |
| W2P SolLab 370 | Yes |
| Shining3D AccuFab-L4K | Yes |
| UnionTech Martrix300 | Yes |
| UnionTech Martrix520 | Yes |
| Asiga Max UV | Yes |
| Asiga Max 2 | Yes |
| Asiga Pro 4K | Yes |
| Asiga Ultra | Yes |
| Prusa SL1S Speed | Yes |
| Anycubic Photon Mono | Yes |
| Anycubic Photon Mono SE | Yes |
| Anycubic Photon Mono X | Yes |
| Anycubic Photon M3 | Yes |
| Anycubic Photon M3 Plus | Yes |
| Anycubic Photon M3 Max | Yes |
| Anycubic Photon Mono M7 Pro | Yes |
| Anycubic Photon D2 | Yes |
| Peopoly Phenom Prime | Yes |
| Creality Halot-One | Yes |
| Creality Halot-One Pro | Yes |
| Uniformation GKTwo | Yes |
| Elegoo Mars 2 | Yes |
| Elegoo Mars 2 Pro | Yes |
| Elegoo Mars 3 | Yes |
| Elegoo Mars 4 | Yes |
| Elegoo Mars 5 | Yes |
| Elegoo Mars 5 Ultra | Yes |
| Elegoo Saturn | Yes |
| Elegoo Saturn 3 | Yes |
| Elegoo Saturn 4 Ultra | Yes |
| Phrozen Sonic Mini 4K | Yes |
| Phrozen Sonic Mini 8K | Yes |
| Phrozen Sonic Mini 8K S | Yes |
| Phrozen Sonic Mighty Revo 14K | Yes |
| Flashforge Hunter S | Yes |
| 385 – 420nm MSLA, SLA & DLP printer | Contact us |
Flame Retardant HDT use cases
Liqcreate Flame Retardant HDT is perfect for applications that require UL94 V0 materials, for instance in electronics, aviation, automobiles, and the railway industry.
Reviews
There are no reviews yet.